This document explains how optimizing the performance of the Selective Soldering machine is achieved by improving the nitrogen environment around the solder pot plate and nozzle assembly.
ITW EAE Support Center
Related Articles
- Investigation if SelectX application is possible
- Lack of flux in leaded joints when using a sprayfluxing system
- Selective soldering of fine pitch components on high thermal mass boards
- High Solderbath Temperature Selective Soldering
- The removal of intermetallic needle shaped crystals from solderbaths
- Improve Through Hole Penetration Selective Nozzles
- Topside preheating ins and outs
- Setting the width of the infeed section finger conveyor and outfeed section
- Setting of a smart wave
- Mechanical setting of chip and smart wave
- Fixing thermocouples for wave and reflow soldering
- Exchanging a solderpot during production
- Notes on general settings for a wave soldering process
- Some notes on the allowable load on the conveyor fingers
- The use and behavior of different preheating systems in wave soldering
- Determination of dropjet nozzle capacity
- How to make a flux usable for the dropjet fluxer
- Multiflux Dogbone Effect
- Preheater Configuration
- Why optimising the wave soldering process is no general panacea of insufficient hole filling
- The use of electromagnetic pumps in soldering equipment
- The function of nitrogen in soldering electronics
- Glowing dross residues of the solderbath
- Solderpot efficiency
- Blowholes in (lead-free) wave soldering
- Flux residues on soldered boards
- Assessment of the quality of wave soldered joints
- Flux penetration in connectors or relays
- "Fixed" position of SMDs during re-reflow